Root canal treatment tool and method for manufacturing the same

ABSTRACT

The present invention relates to a root canal treatment tool that is formed in a shape of a rod and has a work portion formed in a predetermined length from a tip and a shank formed in a manner continuous with the work portion. The work portion has a shape memory characteristic in a range of a predetermined length from the tip and a superelastic characteristic in a remaining portion.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a root canal treatment tool for dental treatment and a method for manufacturing this root canal treatment tool.

2. Description of the Related Art

Tools for treating the root canal of a tooth includes various kinds of tools: for example, a reamer and a file that cut and form a root canal; a compactor, a filler, a spreader, and a plugger that fill the root canal with thermoplastic resin; a cleanser that removes remainders in the root canal; and a broach that fills the root canal with cotton.

The above-described root canal treatment tool is constructed of a slender tapered rod having a work portion provided with a cutting blade or piercing protrusion appropriate for a treatment object or a member having a work portion formed by forming a tapered rod in a spiral shape. Moreover, some kind of tool is constructed of a handle or a grip integrated with the end of the member so that it is gripped or operated by a dentist, or is constructed of a shank so that it is griped by a chuck of a hand piece and the like, or is directly operated by the dentist.

The root canal is excessively thin and has a variety of shapes and sizes and is very different between persons. For this reason, many tools of different sizes are provided even for the same kind of root canal treatment tools. For example, in the case of cutting and forming a root canal by use of a reamer, the reamer is required to be deformed along the shape of the root canal, that is, to have appropriate elasticity so that it should not hurt the surrounding of the root canal.

A technology disclosed in Japanese Patent No. 3375765 is proposed as a root canal treatment tool having extremely high elasticity and shape restoration property as described above. This technology relates to a root canal treatment tool having a work portion formed and manufactured by applying a removing work to a rod-shaped raw material that is subjected to shape memory heat treatment and has a superelastic characteristic while holding it under a memory treatment temperature.

In the above root canal treatment tool, the rod having the work portion formed thereon is flexibly deformed in response to an external force applied thereto and is quickly restored to an original shape when the external force is removed. For this reason, this tool can extremely follow up the shape of the root canal with extremely high fidelity and form the root canal with high accuracy.

In the root canal treatment tool relating to the Japanese Patent No. 3375765, the work portion has the superelastic characteristic uniformly along the whole length and hence when the work portion is bent, a tip portion of a free end also has an action of returning to an original shape. Hence, when the tip portion is inserted into the root canal for the treatment of the root canal and is bent, a repulsive force is generated to act on the wall of the root canal. For this reason, there is a problem of possibility that in the vicinity of a root sharp mouth (tip of the work portion), the work portion might cut the outside of a bent portion more heavily and might cut the inside in the center of the bent portion more heavily to go out of the root canal.

Moreover, since the root canal treatment tool is rotated in a state where the work portion is bent almost along the whole length from the tip at the time of forming the root canal, a repeated bending stress is applied to the work portion. This increases the possibility of breaking a slender tip portion of the work portion. For this reason, although the root canal treatment tool relating to the Japanese Patent No. 3375765 has sufficiently high durability as compared with a root canal treatment tool made of stainless steel, it is required to further enhance the hi-her durability.

SUMAMRY OF THE INVENTION

The object of the invention is to provide a root canal treatment tool that is improved in a point of being apt to go out of the root canal and that is enhanced in durability by weakening the action of returning to an original shape of the tip portion of the work portion, and a method for manufacturing the root canal treatment tool.

In order to solve the above problems, a root canal treatment tool according to the present invention is a root canal treatment tool that is formed in the shape; of a rod and has a work portion formed in a predetermined length from a tip and a shank formed in a manner continuous with the work portion, and is such that the work portion has a shape memory characteristic in the range of a predetermined length from the tip and a superelastic characteristic in a remaining portion.

In the root canal treatment tool, the work portion has the shape memory characteristic in the range of a predetermined length from the tip and the superelastic characteristic in the remaining portion. For this reason, in a state where the tip does not recover a memory shape, even when a small force is applied to the tip from the outside, it is easily deformed in response to this force. That is, the tip having the shape memory characteristic can be freely deformed by a small force as compared with the other portion having the superelastic characteristic.

Therefore, the tip of the work portion loses an action of returning to an original shape and hence well follows up the shape of the root canal and does not deviates from the root canal at the time of forming the root canal. Furthermore, the tip portion becomes soft to improve durability when the work portion is rotated at the time of forming the root canal.

Further, a method for manufacturing a root canal treatment tool according to the present invention is characterized in that: a portion of a wire provided with a superelastic characteristic by a memory heat treatment is subjected to a working of removing metal; and then a portion of the portion subjected to the working of removing metal is again subjected to heat treatment to provide the portion with a shape memory characteristic or a portion of the wire provided with the superelastic characteristic by the memory heat treatment is again subjected to heat treatment to provide the portion with the shape memory characteristic; and then the portion having the shape memory characteristic and the portion that is continuous with the portion having the shape memory characteristic and that has the superelastic characteristic is subjected to the working of removing metal.

According to the above method for manufacturing a root canal treatment tool, the wire provided with the superelastic characteristic is previously subjected to the working of removing metal, thereby being formed into the shape of an objective root canal treatment tool, and then the tip portion of the work portion is again subjected to heat treatment. In this manner, it is possible to manufacture the root canal treatment tool having the work portion that is provided with the shape memory characteristic in the tip and the superelastic characteristic in the remaining portion. Moreover, a portion of the wire provided with the superelastic characteristic is previously again subjected to heat treatment, thereby being provided with the shape memory characteristic, and then is subjected to the working of removing metal, thereby being formed into the shape of the objective root canal treatment tool. In this manner, it is possible to manufacture the root canal treatment tool having the work portion that is provided with the shape memory characteristic in the tip and the superelastic characteristic in the remaining portion.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an illustration to show a reamer as a typical example of a root canal treatment tool.

FIGS. 2A, 2B, and 2C are illustrations to show a method for manufacturing a reamer.

FIG. 3 is a schematic view to illustrate a construction when a fatigue fracture test is conducted on the tip portion of a reamer.

FIGS. 4A, 4B, 4C, 4D, and 4E illustrate a method for heating a wire.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

The preferred embodiment of a root canal treatment tool according to the invention will be described below with reference to drawings and the preferred method for manufacturing the same. FIG. 1 is an illustration to show a reamer as a typical example of a root canal treatment tool. FIGS. 2A, 2B, and 2C are illustrations to show a method for manufacturing a reamer. FIG. 3 is a schematic view to illustrate a construction when a fatigue fracture test is conducted on the tip portion of a reamer.

The root canal treatment tool according to the invention is a tool for treating a root canal and includes all tools formed by use of a rod-shaped material. In this root canal treatment tool, a work portion having a shape capable of performing an objective treatment most reasonably is formed at one end portion and an operation portion operated by a dentist is formed at the other end portion. When the dentist directly operates the tool, this operation portion is formed into a handle and when a tool such as a hand piece is used, the operation portion is provided with a grip formed in a shape suitable for the structure of the grip of the tool.

The shape of a reamer A will be described as an example of the root canal treatment tool with reference to FIG. 1. The reamer A is a tool for cutting a wall of the root canal in a root canal and is constructed of a needle portion 1 and a grip 2.

In the needle portion 1, a tapered work portion 4 extending a predetermined length from a tip 3 is formed and a straight shank 5 is formed in a manner continuous with the work portion 4. The work portion 4 is provided in various cross sections according to the kind of reamer, such as rectangle, triangle, or square so as to exert its unique function.

In the reamer in this embodiment, a rectangular cross section is formed in the shape of a spiral along the work portion 4 to form a groove 4 a and a cutting edge 4 b along the groove 4 a.

The shank 5 has a function of being mounted in the grip 2. The grip 2, as shown in the drawing, is formed so as to be gripped in the chuck of a handle piece or so as to be gripped and operated by a dentist, thereby being formed in the shape and of material corresponding to the respective functions.

For example, the grip 2 shown in the drawing is made of metal such as stainless steel or the like and has a shank 5 inserted into a hole made in its center and fixed thereto with adhesive. Moreover, in the case of forming a grip to be gripped and operated by hand by the dentist, the grip may be also molded by the injection molding of synthetic resin so as to have the shank 5 inserted therein, thereby being integrated with and fixed to the shank 5.

The needle portion 1 is made of metal having a shape memory characteristic, for example, nickel-titan (Ni—Ti) alloy and is formed of a wire having a diameter corresponding to the diameter of the needle portion 1 constructing the reamer A. A portion extending a predetermine length from the tip 3 of the work portion 4 is formed as a shape memory portion 6 having the shape memory characteristic and a portion on the shank 5 side nearer to the shape memory portion 6 in the work portion 4 is formed as a superelastic portion 7 having a superelastic characteristic.

The shape memory portion 6 in the needle portion 1 is provided with such a characteristic by performing heat treatment to the Ni—Ti alloy that does not recover a memory shape in the range of a room temperature or a body temperature. When the shape memory portion 6 reaches a shape recovery temperature and recovers a previously stored shape, it exerts high strength, and when an external force is applied to the shape memory portion 6 in a state where it does not reach the shape recovery temperature, the shape memory portion 6 is easily changed in shape in response to the external force applied thereto. Therefore, the shape memory portion 6 does not have the action of returning to the original shape but can be deformed in a preferable shape.

For this reason, the dentist can bend (pre-curve) the shape memory portion 6 in correspondence with the shape of root canal or the root sharp mouth of a patient at the time of treatment. This pre-curving of the shape memory portion 6 enables the tip 3 and the shape memory portion 6 to follow up the root canal with high fidelity at the time of inserting the tip 3 into the root canal and performing treatment on the root canal. Then, the dentist takes the root canal treatment tool out of the root canal after finishing the treatment and then can deform it to the original shape by applying a force to the shape memory portion 6 or can recover its memory shape by increasing its temperature to the shape recovery temperature.

As described above, the shape memory portion 6 that does not recover the memory shape has high flexibility and a high fatigue resistance characteristic. For this reason, when the work part 4 is bent and rotated in a state where the tip 3 is inserted into the root canal, a fatigue fracture time can be elongated as compared with a tool whose work portion has a superelastic characteristic along the whole length.

The superelastic portion 7 memorizes the shape of a straight needle and keeps a state where a memory shape formed in the shape of the straight needle in the range of room temperature. This superelastic portion 7 has extremely high flexibility and high restorability. That is, the superelastic portion 7 is easily deformed (bent) in response to an external force applied thereto and is easily restored to an original shape when the application of the external force is removed.

In particular, because the work portion 4 is formed in the shape of a taper, when the work portion 4 is bent with a fulcrum at the tip 3, the shank 5 is kept nearly in a straight line and the superelastic portion 7 is bent into the shape of an arc having a small curvature on the shank 5 side and is heavily bent into the shape of an arc that increases a curvature as its portion is closer to the shape memory portion 6 side and the shape memory portion 6 is further heavily bent. That is, the work portion 4 is not uniformly bent but is bent in response to the taper. When the bending of the work portion 4 is released, the superelastic portion 7 is restored to the original shape (in the shape of a straight needle) and the shape memory portion 6 keeps a bent shape.

The length of the shape memory portion 6 in the work portion 4 is not limited to a special value. According to the tests performed by the present inventors, in the work portion having a superelastic characteristic along the whole length, in many cases, the work portion was broken in a portion at 2 mm to 3 mm from the tip. For this reason, the length of the shape memory portion 6 in the work portion 4 needs to be at least 2 mm from the tip 3. Although the maximum length is not limited to a special length, the maximum length is about ¾ of the whole length of the work portion 4. Moreover, when the length of the work portion 6 is 16 mm, the particularly preferable length range of the shape memory portion 6 is from about 3 mm to 6 mm from the tip 3 and more preferably, about 3 mm or 4 mm.

If the length of the shape memory portion 6 is smaller than 2 mm, durability is not substantially different as compared with a reamer having a superelastic characteristic along the whole length of the work portion. Moreover, if the length of the shape memory portion 6 is larger than ¾ of the work portion, at the time of inserting the tip 3 into the root canal and rotating it, there might be presented a problem that the position of a rotational axis is not fixed but is made eccentric to make it difficult to cut the root canal well.

Although the memory shape in the shape memory portion 6 is not limited to a special one, the shape memory portion 6 is preferably formed in the shape of a straight needle as an extension of the superelastic portion 7.

Moreover, it is preferable that the shape recovery temperature of the shape memory portion 6 is sufficiently higher than room temperature and body temperature. That is, when the shape recovery temperature is as high as the body temperature, there might be a possibility that while the root canal is treated, the memory shape is recovered to present the same problem presented when the work portion 4 has the superelastic characteristic along the whole length. Hence, it is necessary that the shape recovery temperature of the shape memory portion 6 is sufficiently higher than the room temperature or the body temperature. Such a temperature includes a processing temperature at the time of autoclave sterilization but, needless to say, it is not intended to limit the shape recovery temperature to this temperature.

In the case of using the above reamer A, it is possible to cut the wall of the root canal and to form the root canal in the following manner: a dentist makes the chuck of a hand piece (not shown) grip the grip 2 and holds the hand piece and bends the shape memory portion 6 formed on the tip 3 side of the work portion 4 in correspondence to the shape of the patient's root canal and then inserts the tip 3 into the root canal and moves it in the axial direction while rotating it in a direction of the cutting edge 4 b.

Incidentally, because the reamer A as a root canal treatment tool is taken as an example in this embodiment, the cutting edge 4 b is formed on the reamer A. However, all of the root canal treatment tools do not necessarily have the cutting edge 4 b formed on their work portions 4 but some of them have a needle-shaped protrusion or a tapered coil formed on the work portions. Even in such a root canal treatment tool, by forming the shape memory portion 6 within a predetermined range from the tip 3 of the work portion 4 and by forming the remaining portion of the superelastic portion 7, it is possible to prevent the tool from being withdrawn from the root canal and to improve durability.

Next, a first manufacturing method for manufacturing the reamer A will be described with reference to FIGS. 2A, 2B, and 2C. The first manufacturing method is a method by which a raw material previously provided with a superelastic characteristic is subjected to a working of removing metal to form a work portion and by which the tip side of the work portion is again subjected to a heat treatment to provide the tip side with a shape memory characteristic.

As shown in FIG. 2A, a wire made of a Ni—Ti alloy previously provided with a superelastic characteristic and having a diameter corresponding to the size of the objective reamer A is cut in correspondence with the length of the reamer A to form a rod-shaped raw material 11.

As shown in FIG. 2B, the raw material 11 is worked into the shape of a taper and is worked to form the groove 4a and the cutting edge 4 b and is further worked to form the tip 3, whereby the work portion 4 and the shank 5 are formed. In this manner, the needle portion 1 is formed. At the time of working the raw material 11, the raw material 11 can not be plastically worked because it has a superelastic characteristic. For this reason, the workings of tapering the raw material 11 and forming the groove 4 a and the cutting edge 4 b are performed by a working of removing metal, including a cutting working. The work portion 4 formed in this manner has the superelastic characteristic along the whole length thereof.

Next, the shape memory portion 6 is formed in a range of a predetermined length from the tip 3 of the work portion 4. This process, as shown in FIG. 2C, is performed as follows: portions other than a portion corresponding to the shape memory portion 6 in the needle portion 1 are cooled by a cooling agent 12 and the shape memory portion 6 is heated on the basis of heat treatment conditions set for the raw material 11 in a state where the shape memory portion 6 is kept in an objective shape (in the shape of a straight needle in this embodiment). Any one of the following methods can be selected as a specific example of a method for forming the shape memory portion 6.

(A) Partial heating method by hot air (see FIG. 4A)

A portion 1B not to be heat-treated is partially dipped in water 21 as a cooling agent so as to prevent a temperature increase or is blown by cool air and, at the same time, a portion 1A to be heat-treated is blown by hot air 22, thereby being partially heated.

(B) Partial heating method by a furnace (see FIG. 4B)

A furnace 23 is partitioned into two layers and a portion 1A to be heat-treated is partitioned by heat insulating material 24 so as to prevent a portion 1B not to be heat-treated from being increased in temperature and is heated in the furnace 23. Here, if a portion 1A can be surely insulated from heat, the furnace 23 is not required to be partitioned.

(C) Partial heating method by liquid (see FIG. 4C)

A portion 1B not to be heat-treated is held by a clip 25 provided with a cooling function and a portion 1A to be heat-treated is dipped in liquid in a salt bath 26 at high temperatures, thereby being heated.

(D) Partial heating method by solid (see FIG. 4D)

A portion 1B not to be heat-treated is dipped in a cooling agent 27 such as water to prevent a temperature increase and a portion 1A to be heat-treated is brought into contact with or close to a heating body 28 at high temperatures, thereby being heated.

(E) Partial heating method by heating pod (see FIG. 4E)

A small hole 30 through which a work piece (wire) can be inserted is made in a heating pod 29 and only a portion 1A to be heat-treated is inserted into this small hole 30, thereby being partially heated. Here, a portion not to be inserted into the heating pod 29 (portion not to be heat-treated) 1B may be blown by cool air, thereby being actively cooled.

The cooling agent 12 for cooling a portion other than the shape memory portion 6 at the time of heat-treating the shape memory portion 6 is not limited to a special one but, for example, water can be used.

The shank 5 of the needle portion 1 provided with the shape memory portion 6 in the range of a predetermined length from the tip 3 is inserted into and bonded to a grip (not shown), whereby the objective reamer A can be manufactured.

A second manufacturing method according to the present invention is a method by which the raw material 11 shown in FIG. 2A is heat-treated in the range of a predetermined length from a tip on one side at the step of forming the raw material 11 to provide it with the shape memory characteristic and by which the raw material 11 is then subjected to a working including the removal of metal to form the work portion 4 having the groove 4 a and the cutting edge 4 b to manufacture an objective reamer A.

According to the above second manufacturing method, at the step of the raw material 11, a portion having the shape memory characteristic and a portion having the superelastic characteristic are formed and then the raw material 11 is subjected to the working of removing metal to form the work portion 4. Therefore, in the shape memory portion 6 is memorized the shape of a straight needle and are formed the groove 4 a and the cutting edge 4 b continuous with the superelastic portion 7 formed thereon.

As described above, the raw material 11 having the portion corresponding to the shape memory portion and the portion corresponding to the superelastic portion is subjected to the working including the removal of metal to form the needle portion 1 including the work portion 4 and the shank 5 and then the shank 5 is inserted into and bonded to the grip (not shown), whereby the objective reamer A can be manufactured.

The present inventors manufactured five samples (conventional samples) each of which was a No. 30 reamer formed of a raw material of about 1.0 mm in diameter and having a tip portion of about 0.3 mm in diameter, a taper of 4/100, a rectangular cross section, a needle portion protruding from the grip 2 and having a length of about 25 mm, and a work portion having a length of about 15 mm, wherein the work portion had a superelastic characteristic along the whole length thereof, five, samples (first method samples) each of which had the shape memory portion 6 formed in the range of about 4 mm from the tip 3 and had the superelastic portion 7 formed in the remaining work portion 4 by the first manufacturing method; and five samples (second method samples) each of which had the shape memory portion 6 formed in the range of about 4 mm from the tip 3 and had the superelastic portion 7 formed in the remaining work portion 4 by the second manufacturing method, and then conducted tests of bending tests and fatigue fracture tests.

Incidentally, the heat treatment for forming the shape memory portion 6 in the work portion 4 is performed to the thin rod within a limited range and hence a boundary is not clearly produced between the shape memory 6 and the superelastic portion 7. For this reason, it is difficult to express the range of length from the tip 3 of the shape memory portion 6 by an exact numerical value and hence there is no other choice but to express that the shape memory portion 6 is formed in the range of about 4 mm.

In the bending test, the work portion 4 was gripped at a position of about 3 mm from the tip 3 and torque when the work portion 4 was bent about 45 degrees in this state was measured. As a result, the average value of the conventional samples was about 51 gf-cm and the average value of the first method samples was about 43 gf-cm and the average value of the second method samples was about 45 gf-cm.

From the above measurement results, it can be said that the reamer A having the shape memory portion 6 in the range of about 4 mm from the tip 3 of the work portion 4 can be bent by smaller torque as compared with a reamer having the superelastic characteristic along the whole length. That is, the reamer A according to this embodiment has higher flexibility in the range of about 4 mm from the tip 3 as compared with the conventional reamer.

Therefore, even if the shape memory portion 6 is forcibly bent and then a force required to bent it is released, the bending shape of the shape memory portion 6 can be kept. For this reason, at the time of treating the root canal, it is possible to bend the shape memory portion 6 previously according to the shape of the patient's root canal and to insert the tip 3 into the root canal and to perform treatment with this bent shape kept. That is, it is possible to make the shape memory portion 6 exert a guidance function to the root canal.

Moreover, even when treatment for the root canal progresses and where the tip 3 reaches the root sharp mouth, because the shape memory portion 6 is easily bent, the shape memory portion 6 does not apply a repulsive force to the wall of the root canal. Therefore, this prevents the shape memory portion 6 from cutting the wall of the root canal more heavily near the root sharp mouth and in the center of curve and deviating from the root canal.

The fatigue fracture tests were conducted by use of an apparatus shown in FIG. 3. That is, by use of the apparatus having a pair of pins 21, 22 having grooves 21 a, 22 a capable of receiving the tip 3 side of the work portion 4, the work portion 4 was set such that a position of 4 mm from the tip 3 of the work portion 4 corresponded to the center of one pin 21 and that the tip 3 was inserted into the groove 22 a of the other pin 22 to bend the shape memory portion 6 in the work portion 4 about 45 degrees, and then the work portion 4 was rotated at 200 rpm while keeping this state of bending and then the time that elapsed before the shape memory portion 6 was brought into fracture was measured.

As the results of the above fatigue fracture tests, the conventional samples were brought into fracture in about 5 minutes on average, and the first method samples were brought into fracture in about 14 minutes on average, and further the second method samples were brought into fracture in about 11 minutes on average.

From the test results, it can be said that the reamer A having the shape memory portion 6 in the range of about 4 mm from the tip 3 of the work portion 4 has sufficiently high durability as compared with the reamer having the superelastic characteristic along the whole length.

As described above in detail, in the root canal treatment tool according to the present invention, by forming the shape memory portion having the shape memory characteristic in the range of a predetermined length range from the tip of the work portion and the superelastic portion having the superelastic characteristic in a manner continuous with the shape memory portion, it is possible to make the shape memory portion exert flexibility and be easily deformed.

For this reason, at the time of starting the treatment of the root canal, by bending the shape memory portion in correspondence to the shape of the patient's root canal, it is possible to make the shape memory portion exert a function as a guide. Moreover, since the shape memory portion can be flexibly deformed in response to the action of external force, even if the tip of the work portion reaches the root sharp mouth, the shape memory portion does not cut the wall of the root canal more than required and hence can be prevented from deviating from the root canal.

Further, since the shape memory portion has extremely high flexibility, the shape memory portion can exert high durability for repeated bends and hence can elongate the time that elapses before it is brought into fatigue fracture as compared with the root canal treatment tool having the superelastic characteristic along the whole length of the work portion.

Still further, according to the first manufacturing method and the second manufacturing method according to the present invention, a wire having a superelastic characteristic is previously subjected to a working of removing metal to be formed into the shape of an objective root canal treatment tool; and then the tip portion of a work portion is again subjected to heat treatment or a portion of the wire exerting the superelastic characteristic is again subjected to heat treatment to exert a shape memory characteristic; and then the portion having the shape memory characteristic and the portion that is continuous with the portion having the shape memory characteristic and has the superelastic characteristic are subjected to the working of removing metal. In this manner, the root canal treatment tool that has the work portion having the shape memory characteristic in the tip and the superelastic characteristic in the remaining portion can be manufactured.

Incidentally, although the heat treatment of the predetermined portion of the wire is performed by the above methods, it is not intended to limit the method of heat treatment these methods but the work piece can be worked into a heat-treated portion and a non-heat-treated portion by various methods. 

1. (canceled)
 2. A method for manufacturing a root canal treatment tool, the method comprising the steps of: subjecting a portion of a wire, provided with a superelastic characteristic by a first memory heat treatment, to a working of removing metal; and subjecting a part in a certain length from a tip of the wire, of the portion to be provided with the working of removing metal to a second heat treatment to provide the part with a shape memory characteristic.
 3. The method for manufacturing a root canal treatment tool according to claim 2, wherein the step of subjecting the portion to a second heat treatment is performed by heat-protecting a portion not to be subjected to the second heat treatment by a cooling agent, and heating the portion to be subjected to the second heat treatment by predetermined means.
 4. A method for manufacturing a root canal treatment tool, the method comprising the steps of: subjecting a portion of a wire, in a certain length from a tip of the wire, provided with a superelastic characteristic by a first memory heat treatment, to a second heat treatment to provide the portion of the wire with a shape memory characteristic; and subjecting the portion of the wire having the shape memory characteristic, and a portion of the wire that is continuous with the portion having the shape memory characteristic and which has the superelastic characteristic, to working of removing metal.
 5. The method for manufacturing a root canal treatment tool according to claim 4, wherein the step of subjecting the portion to a second heat treatment is performed by heat-protecting a portion not to be subjected again to heat treatment by a cooling agent and heating the portion to be subjected to the second heat treatment by predetermined means. 